TYPE					Method
Item			OPET	OPET
Features			High Barrier	High Barrier
WVTR*1	40°C, 90%RH	g/㎡/day	0.08	0.15	ASTM F-1294*1
O2TR*1	25°C, 80%RH	cc/㎡/day/atm	0.1	0.3	ASTM D-3985*1
Haze		%	4	4	ISO 13468-1
Light Transmission Rate		%	89	89	ISO 13468-1
Tensile Strength	MD	Mpa	220	220	ISO 527-3
		Kg/㎟	22	22
	TD	Mpa	230	230
		Kg/㎟	23	23
Tensile Elongation	MD	%	110	110	ISO 527-3
	TD	%	110	110
Puncture Impact Strength		J/piece	0.7	0.7	Puncture test
		Kg·cm/piece	7	7
Dynamic coefficient friction  Substrate / Substrate			0.45	0.45	ISO 8295
Shrinkage (Dry heat)	MD	%	1	1	180°C, 5min
	TD	%	-0.1	-0.1
Shrinkage (Hot water)	MD	%	-	-	95°C, 5min
	TD	%	-	-
Yield		g/㎡	16.8	16.8
Food Sanitation Law (JAPAN)
FDA*2
EUD*2

Preliminary evaluation by customer is strongly recommended.

• *1:Data as laminated film.
• *2:is adopting FDA and EUD.