TECHBARRIER -V, P2, H, T, TZ
| Type |
V |
P2 |
H |
T |
TZ |
Method |
| Base Film |
OPET |
| Characterisitics |
Standard Clarity |
Humidity barrier Easy Adhesion Easy Printing |
High barrier Boiling |
High barrier Retort |
Retort Clarity |
Oxygen Transmission Rate 25 , 80%RH |
fmol/m2 s Pa |
3.5 | 2.5 | 1.5 | 1.5 | 5.0 |
JIS K 7126 as Laminated film |
{cc/m2 d atm} |
{0.7} | {0.5} | {0.3} | {0.3} | {1.0} |
Water vapor Transmission Rate 40 , 90%RH |
g/m2 d |
0.7 | 0.3 | 0.3 | 0.3 | 1.0 |
JIS K 7129 as Laminated film |
| Haze |
% |
4.0 | 4.0 | 4.0 | 4.0 | 4.0 |
JIS K 7361 |
| Light Transmission Rate |
% |
89 | 89 | 89 | 86 | 89 |
| Elongation Strength |
MD |
MPa |
220 | 220 | 220 | 220 | 220 |
JIS K 7127 |
| Kg/mm2 |
22 | 22 | 22 | 22 | 22 |
| TD |
MPa |
230 | 230 | 230 | 230 | 230 |
| Kg/mm2 |
23 | 23 | 23 | 23 | 23 |
| Elongation |
MD |
% |
110 | 110 | 110 | 110 | 110 |
JIS K 7127 |
| TD |
% |
110 | 110 | 110 | 110 | 110 |
| Impact Strength |
J/piece |
0.7 | 0.7 | 0.7 | 0.7 | 0.7 |
Puncture Test |
| Kg-cm/piece |
7 | 7 | 7 | 7 | 7 |
| COF |
nonSiOx / nonSiOx |
0.45 | 0.45 | 0.45 | 0.45 | 0.45 |
JIS K 7125 |
| Heat Shrinkage (dry) |
MD |
% |
1.0 | 1.0 | 1.0 | 1.0 | 1.0 |
180 , 5 min |
| TD |
% |
-0.1 | -0.1 | -0.1 | -0.1 | -0.1 |
| Heat Shrinkage (hot water) |
MD |
% |
- | - | - | - | - |
95 , 5 min |
| TD |
% |
- | - | - | - | - |
Wet ability SiOx |
mN/m |
54< | 54< | 54< | 54< | 54< |
JIS K 6768 |
| dyne/cm |
54< | 54< | 54< | 54< | 54< |
|
|
TECHBARRIER -NY, NR, S
| Type |
NY |
NR |
S |
Method |
| Base Film |
ONY |
OPVA |
| Characterisitics |
Liquid Sachet Anti Pinhole |
Retort Anti Pinhole |
Super High barrier |
Oxygen Transmission Rate 25 , 80%RH |
fmol/m2 s Pa |
2.5 | 2.5 | <0.5 |
JIS K 7126 as Laminated film |
{cc/m2 d atm} |
{0.5} | {0.5} | {<0.1} |
Water vapor Transmission Rate 40 , 90%RH |
g/m2 d |
0.7 | 0.7 | 0.1 |
JIS K 7129 as Laminated film |
| Haze |
% |
2.0 | 2.0 | 1.0 |
JIS K 7361 |
| Light Transmission Rate |
% |
90 | 90 | 86 |
| Elongation Strength |
MD |
MPa |
260 | 260 | 280 |
JIS K 7127 |
| Kg/mm2 |
26 | 26 | 28 |
| TD |
MPa |
270 | 270 | 300 |
| Kg/mm2 |
27 | 27 | 30 |
| Elongation |
MD |
% |
120 | 120 | 90 |
JIS K 7127 |
| TD |
% |
110 | 110 | 80 |
| Impact Strength |
J/piece |
1.6 | 1.6 | 0.9 |
Puncture Test |
| Kg-cm/piece |
16 | 16 | 9 |
| COF |
nonSiOx / nonSiOx |
0.45 | 0.55 | 0.45 |
JIS K 7125 |
| Heat Shrinkage (dry) |
MD |
% |
3.0 | 3.0 | 2.5 |
180 , 5 min |
| TD |
% |
3.0 | 3.0 | 1.5 |
| Heat Shrinkage (hot water) |
MD |
% |
1.9 | 1.9 | - |
95 , 5 min |
| TD |
% |
2.0 | 2.0 | - |
Wet ability SiOx |
mN/m |
54< | 54< | 54< |
JIS K 6768 |
| dyne/cm |
54< | 54< | 54< |
The above data is NOT guaranteed.
|