| Article |
Unit |
SP-R SH
shrink type |
Method |
| Thickness |
 m |
15 |
JIS Z 1714 |
| Haze |
% |
4 |
JIS Z 1714 |
| Tensile Strength |
MPa
{Kg/mm2} |
MD |
280
{28} |
JIS Z 1714 |
| TD |
300
{30} |
| Elongation |
% |
MD |
120 |
JIS Z 1714 |
| TD |
90 |
| Impact Strength |
J/piece
{Kg-cm/piece} |
1.5
{15} |
Puncture Test |
| Stick Strength |
N/piece
{g/piece} |
6.5
{650} |
diameter 0.5mm |
| Flex Pinhole |
number/0.05m2 |
5 |
Gelbo-Flex Test
23 , 3000times |
| Shrinkage with hot water |
% |
MD |
18 |
95, 5 min |
| TD |
20 |
| COF |
|
non-Corona
/non-Corona |
0.6 |
JIS K 7125 |
| Oxygen Permeability |
fmol/(m2 sPa)
{cc/(m2datm)} |
40
{8} |
JIS Z 1714
23, 50%RH |
| Water vapor Permeability |
g/(m2d) |
100 |
JIS Z 0208
40, 90%RH |
| Wet Tension |
mN/m
{dyne/cm} |
corona |
54
{54} |
JIS Z 1714 |
| non-corona |
40
{40} |
The above data is NOT guaranteed.
|